- News
- Books
Featured Books
- pcb007 Magazine
Latest Issues
Current IssueThe Essential Guide to Surface Finishes
We go back to basics this month with a recount of a little history, and look forward to addressing the many challenges that high density, high frequency, adhesion, SI, and corrosion concerns for harsh environments bring to the fore. We compare and contrast surface finishes by type and application, take a hard look at the many iterations of gold plating, and address palladium as a surface finish.
It's Show Time!
In this month’s issue of PCB007 Magazine we reimagine the possibilities featuring stories all about IPC APEX EXPO 2025—covering what to look forward to, and what you don’t want to miss.
Fueling the Workforce Pipeline
We take a hard look at fueling the workforce pipeline, specifically at the early introduction of manufacturing concepts and business to young people in this issue of PCB007 Magazine.
- Articles
- Columns
Search Console
- Links
- Media kit
||| MENU - pcb007 Magazine
Estimated reading time: 1 minute

Contact Columnist Form
Copper Discoloration and Other Concerns with OSP
Yes, it is about process. And that includes equipment operating parameters as well as chemistry. Getting the OSP process to perform as it is intended requires attention to both. This month's "Trouble in Your Tank" delves into one of the most irritating issues with respect to OSP: discoloration (read "oxidation") on critical circuit features. Why did this occur? Is there more than one cause? Will solderability be compromised? These are just a few of the questions raised when such a situation occurs. An example of this occurrence is shown in Figure 1.
Discoloration and even oxidation of the copper may occur for one of several reasons. Some of those listed may be more or less obvious than the others (Table 1). Some of these causes can be both equipment and chemistry related.
Figure 2 shows another example of discoloration on the copper pad most likely related to oxidation of the underlying copper. Further analysis of this situation pointed to two possible causes. The first was very low thickness of the OSP coating. In this case the thickness was less than the minimum recommended by the supplier (measured OSP thickness 0.08 micron versus recommended 0.20–0.25 micron). Certainly, the low thickness is cause for concern. With such a low thickness, the OSP would not effectively protect the copper from oxidation. However, what other process variations could be the cause for the low thickness? One possibility is the micro-etch step. It has been stated in the literature that a clean active copper surface is necessary in order to allow for a more uniform deposit of the OSP film. In addition, one should avoid an overly aggressive microetch as there are concerns about insufficient thickness of the organic film in deep crevasses.
Surface roughness does have an impact on OSP film thickness and is directly connected to solderability.
Editor's Note: This article originally appeared in the April issue of The PCB Magazine.
More Columns from Trouble in Your Tank
Trouble in Your Tank: Interconnect Defect—The Three Degrees of SeparationTrouble in Your Tank: Things You Can Do for Better Wet Process Control
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 5
Trouble in Your Tank: Materials for PWB Fabrication—Drillability and Metallization
Trouble in Your Tank: Supporting IC Substrates and Advanced Packaging, Part 5
Trouble in Your Tank: Electrodeposition of Copper, Part 6
Trouble in Your Tank: Electrolytic Copper Plating, Part 5
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 4