- News
- Books
Featured Books
- pcb007 Magazine
Latest Issues
Current IssueThe Essential Guide to Surface Finishes
We go back to basics this month with a recount of a little history, and look forward to addressing the many challenges that high density, high frequency, adhesion, SI, and corrosion concerns for harsh environments bring to the fore. We compare and contrast surface finishes by type and application, take a hard look at the many iterations of gold plating, and address palladium as a surface finish.
It's Show Time!
In this month’s issue of PCB007 Magazine we reimagine the possibilities featuring stories all about IPC APEX EXPO 2025—covering what to look forward to, and what you don’t want to miss.
Fueling the Workforce Pipeline
We take a hard look at fueling the workforce pipeline, specifically at the early introduction of manufacturing concepts and business to young people in this issue of PCB007 Magazine.
- Articles
- Columns
Search Console
- Links
- Media kit
||| MENU - pcb007 Magazine
Estimated reading time: 1 minute

Contact Columnist Form
Getting to the Root Cause - Solderability Defect Analysis
In this case study, the PCB fabricator investigates the root cause of solderability defects on ENIG-processed circuits. It was determined that the fabricator, due to process errors, caused hyper-corrosion within the nickel deposit, which led to the defects.
Introduction
A PCB fabricator received a number of returned PCBs from one of its assembly customers. The issue, according to the assembly team, was dewetting, and in some cases, non-wetting of surface mount pads. In addition, some of those components failed to make a reliable bond to the pad, leading to significant failures. And as so often is the case, someone invokes the ghost of black pad as the culprit. Certainly while such an anomaly is a possibility with respect to the root cause failure mechanism, this case requires significant study in order to properly reach a solution to the problem.
Problem Identification
First, one must identify the problem or defect (Figure 1 and Figure 2).
Figure 1: Note area where solder did not completely wet-out.
I consider this a very minor issue considering the board design, reflow temperatures, and paste print could have a great deal to do with what is seen here.
Figure 2: Some additional dewetting.
Read the full column here.Editor's Note: This column originally appeared in the December 2014 issue of The PCB Magazine.
More Columns from Trouble in Your Tank
Trouble in Your Tank: Interconnect Defect—The Three Degrees of SeparationTrouble in Your Tank: Things You Can Do for Better Wet Process Control
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 5
Trouble in Your Tank: Materials for PWB Fabrication—Drillability and Metallization
Trouble in Your Tank: Supporting IC Substrates and Advanced Packaging, Part 5
Trouble in Your Tank: Electrodeposition of Copper, Part 6
Trouble in Your Tank: Electrolytic Copper Plating, Part 5
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 4