- News
- Books
Featured Books
- pcb007 Magazine
Latest Issues
Current IssueThe Essential Guide to Surface Finishes
We go back to basics this month with a recount of a little history, and look forward to addressing the many challenges that high density, high frequency, adhesion, SI, and corrosion concerns for harsh environments bring to the fore. We compare and contrast surface finishes by type and application, take a hard look at the many iterations of gold plating, and address palladium as a surface finish.
It's Show Time!
In this month’s issue of PCB007 Magazine we reimagine the possibilities featuring stories all about IPC APEX EXPO 2025—covering what to look forward to, and what you don’t want to miss.
Fueling the Workforce Pipeline
We take a hard look at fueling the workforce pipeline, specifically at the early introduction of manufacturing concepts and business to young people in this issue of PCB007 Magazine.
- Articles
- Columns
Search Console
- Links
- Media kit
||| MENU - pcb007 Magazine
Estimated reading time: 1 minute

Contact Columnist Form
Trouble in Your Tank: Case Study: Plating Nodules— Where Did These Come From?
Introduction
Sometimes the problems can really get pretty ugly. One would assume these uglies would be easy to correct. But most often, solving such a problem requires a much deeper dig into the process. In this column this principle will be illustrated with a real-life case study. In this real-life troubleshooting exercise, plating anomalies were detected on the PWBs plated in two different plating cells. This study points out that the root of the defects is rooted in two different causes. One is related to addition agent control, the other to solution filtration and anode maintenance. The study digs into plating roughness and multiple causes and corrective actions.
Severe Plating Roughness/Nodules
In previous columns, this author has presented many possibilities for copper plating nodules. However, what occurred with one PWB fabricator was on the extreme (Figure 1).
In Figure 2, a somewhat different type of nodule appeared on circuits at the same fabricator. Only this defect occurred on circuit boards plated in a different cell.
Basically this fabricator was seeing two different types of nodules/roughness. The nodules depicted in Figure 1 clearly show “normal” copper grain structure (fine-grained equiaxed). However, in Figure 2, the grain is quite large. In addition, the nodule/roughness shown in Figure 1 can be traced to what looks like debris that has been essentially plated up and around.
Editor's Note: This column originally appeared in the October 2016 issue of The PCB Magazine.
More Columns from Trouble in Your Tank
Trouble in Your Tank: Interconnect Defect—The Three Degrees of SeparationTrouble in Your Tank: Things You Can Do for Better Wet Process Control
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 5
Trouble in Your Tank: Materials for PWB Fabrication—Drillability and Metallization
Trouble in Your Tank: Supporting IC Substrates and Advanced Packaging, Part 5
Trouble in Your Tank: Electrodeposition of Copper, Part 6
Trouble in Your Tank: Electrolytic Copper Plating, Part 5
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 4